Star U66-2 Two-Part Brush-On Epoxy
MFR #:U66-2
EIS #:PH21-U66-2
MFR #:U66-2
EIS #:PH21-U66-2
Two part epoxy designed for use as an electrical general purpose brush-on compound ideal for general maintenance. When mixed, U-66-2 will require no baking to achieve the ultimate curing properties. U-66-2 will cure tack free in 4 - 8 hours and cure completely after 96 hours (4 days) at room temperature. U-66-2 will completely cure after baking for 5 minutes at 100 °C. - Designed for electrical general purpose brush-on compound ideal for general maintenance. Fast room temperature cure in thin films.
$33.34
- $104.10
Select from the options below
Two part epoxy designed for use as an electrical general purpose brush-on compound ideal for general maintenance. When mixed, U-66-2 will require no baking to achieve the ultimate curing properties. U-66-2 will cure tack free in 4 - 8 hours and cure completely after 96 hours (4 days) at room temperature. U-66-2 will completely cure after baking for 5 minutes at 100 °C. - Designed for electrical general purpose brush-on compound ideal for general maintenance. Fast room temperature cure in thin films.
Product Options
Showing 2 out of 2 options
 | Container Size: 50 g | EIS Part #: STARU66-250GM | $ / Kit | |
| Container Size: 1 lb | EIS Part #: STARU66-21LB | $ / US pound |
- Attributes
- Features
- Applications
- Documents
Attributes
General Information
Item NameBrush-On Epoxy
SeriesU66-2
General Features
TypeTwo-Part
Design & Construction
Base TypeEpoxy
ColorBrick Red (Mixed Product)
Color - Part-ABrick Red
Color - Part-BLight Straw
Performance Details
Flexural Strength15000 psi
Full Cure Time4 - 8 hr
Tensile Strength6000 psi
Chemical Properties
Mixing Ratio100:17 (By Weight)
Specific Gravity1.13 g/cc
Specific Gravity - Part-A1.38 g/cc
Specific Gravity - Part-B1.02 g/cc
Viscosity33000 cP
Viscosity - Part-B1200 cP
Electrical Properties
Dielectric Strength429 V/mil
Physical Properties
Container TypeKit
Elongation4%
Hardness80 Shore D
Features
- class H temperature use
- 25 min (250g mass at 75 °F) pot life
- 1300 PSI at 23 °C, 100 PSI at 150 °C lap shear
- 363,000 psi tensile modulus
- 400000 PSI flexural modulus
- 105 °C glass transition temperature
- 1.58% (28 days at 188 °C) weight loss
- 0.64% [28 days at 25 °C] water absorption
- 9.87 X 10^-3 (48 hr water immersion), 9.57 X 10^-3 (48 hr 50% relative humidity) dissipation factor
- 1.56 (48 hr Water Immersion), 1.61 (48 hr 50% relative humidity) dielectric constant
- 9.63 X 10^15 (48 hr water immersion), 9.49 X 10^15 (48 hr 50% relative humidity) volume resistivity
- 12 months Shelf life
- Dielectric Strength: 429 V/Mil (25 °C, 1/8 Inch)
- Viscosity: 33000 cps at 20 rpm
- Flexural Strength: 15000 psi (ASTM D790)
- Tensile Strength: 6000 psi (ASTM D638)
Applications
- For General Maintenance