Loctite 648 High Strength Retaining Compound, 1L Bottle, Green, MFR ID 1835917
- MFR #LOC-648
- EIS #LOC1835917
- Series #LOC-648
- UPC #00079340006515
$722.67 / liter
Available to Order
Refine your product below or compare all choices in the
Min QTY1QTY Increment1
more info
| Stock Status | |||
|---|---|---|---|
 | 1L | $ / liter more info | |
 | 50mL | $ / Bottle Pack: 10/Case | |
 | 250 mL | $ / Piece more info |
Loctite 648 high strength, rapid cure retaining compound performs best for clearance or interface fit parts. Excellent performance for dynamic, axial and radial loads. Bonds through contaminants including oils, cutting and corrosion protection fluids. Cures on metals without an activator.
Loctite 648 is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration.
Applications
- For Press Fitted Parts
Features
- Best performance for clearance or interference fit parts
- Excellent performance for dynamic, axial and radial loads
- Bonds through contaminants including oils, cutting and corrosion protection fluids
- Cures on metals without an activator
- Globally available product
General Information
| Item Name | Retaining Compound |
| Trade Name | Henkel |
| Series | LOC-648 |
General Features
| Type | High Strength |
| Standards | NSF/ANSI 61 Approved |
| Storage Temperature | 8 to 21 °C |
Design & Construction
| Color | Green |
| Cure Type | Anaerobic Cure |
| Form | Liquid |
Performance Details
| Application Time | 5 min |
| Full Cure Time | 24 hr |
| Shear Strength | 3900 psi |
Chemical Properties
| Composition | Urethane Methacrylate |
| Specific Gravity | 1.13 |
| Viscosity | 500 cP |
| VOC | <3% |
Physical Properties
| Container Size | 1L |
| Container Type | Bottle |
| Odor/Scent | Characteristic |
Environmental Condition
| Temperature Rating | -65 to 300 °F |
Supporting Information
| Applicable Materials | Mild Steel, Stainless Steel and Plated Surfaces |
Documents
No Documents Found