DuPont Kapton® HN General Purpose Polyimide Film Sheet, 5 Mil x 25" x 36", MFR ID KAPHN504
- MFR #Kapton® HN-SHT
- EIS #KAPHN504
- Series #Kapton® HN-SHT
$92.88 / Sheet
In Stock | Ready to Ship
Refine your product below or compare all choices in the
Min QTY1QTY Increment1
more info
| Stock Status | ||||
|---|---|---|---|---|
 | 1 mil | 25 Inch | $ / Sheet more info | |
| 2 mil | 25 Inch | $ / Sheet more info | |
| 3 mil | 25 Inch | $ / Sheet | |
| 5 mil | 25 Inch | $ / Sheet more info |
DuPont™ Kapton® HN general-purpose film has been used successfully in applications at temperatures as low as -269°C (-452°F) and as high as 400°C (752°F). HN film can be laminated, metallized, punched, formed or adhesive coated. - Kapton® HN is the recommended choice for applications that require an all-polyimide film with an excellent balance of properties over a wide range of temperatures.
Features
- Kapton� HN has been used successfully in applications at temperatures as low as -269 °C and as high as 400 °C. Kapton� HN film can be laminated, metallized, punched, formed or adhesive coated
- Thermally conductive
- Excellent electrical properties
- Mechanical toughness
- Withstands extreme temperatures and harsh environments
- Retains its properties for extended storage periods
- Low moisture uptake and high moisture resistance
- Temperature Rating: -269 to 400 °C
- Tensile Strength: 139 - 231 Mpa
- Tensile Strength: 139 to 231 MPa (Ultimate)
- Volume Resistivity: 1 Ohm-cm x 10^17 Ohm-cm
Applications
- Mechanical Parts
- Electronic Parts
- Electrical Insulation
- Pressure Sensitive Tape
- Fiber Optics Cable
- Insulation Blankets
- Insulation Tubing
- Automotive Diaphragms Sensors and Manifolds
- Etching
General Information
| Item Name | Polyimide Film |
| Trade Name | Kapton® |
| Series | Kapton® HN-SHT |
General Features
| Type | General Purpose |
Performance Details
| Tensile Strength | 139 Mpa |
Physical Properties
| Elongation | 82 to 83% |
| Thickness | 5 Mil |
| Width | 25 Inch |
| Density | 1.42 g/cc |
| Length | 36 Inch |