DuPont Kapton® HN General Purpose Polyimide Film Roll, 1 Mil x 0.32" x 1700', MFR ID KAPHN001X.320
- MFR #Kapton® HN-ROL
- EIS #KAPHN001X.320
- Series #Kapton® HN-ROL
$224.45 / US pound
Available to Order
Refine your product below or compare all choices in the
Min QTY1QTY Increment1
more info
| Stock Status | |||||
|---|---|---|---|---|---|
 | 5000 ft | 1 mil | 52 Inch | $ / US pound more info | |
| 1700 ft | 1 mil | 0.25 Inch | $ / Roll more info | |
| 1700 ft | 1 mil | 0.32 Inch | $ / US pound more info | |
| 1700 ft | 1 mil | 0.75 Inch | $ / Roll more info | |
| 1700 ft | 1 mil | 1 Inch | $ / Roll | |
| 1700 ft | 1 mil | 1.25 Inch | $ / Roll |
DuPont Kapton® HN General Purpose Polyimide Film. - Kapton® HN is the recommended choice for applications that require an all-polyimide film with an excellent balance of properties over a wide range of temperatures.
Features
- Kapton� HN has been used successfully in applications at temperatures as low as -269 °C and as high as 400 °C. Kapton� HN film can be laminated, metallized, punched, formed or adhesive coated
- Thermally conductive
- Excellent electrical properties
- Mechanical toughness
- Withstands extreme temperatures and harsh environments
- Retains its properties for extended storage periods
- Low moisture uptake and high moisture resistance
- Temperature Rating: -269 to 400 °C
- Tensile Strength: 139 - 231 Mpa
- Tensile Strength: 139 to 231 MPa (Ultimate)
- Volume Resistivity: 1.5 Ohm-cm x 10^17 Ohm-cm
Applications
- Mechanical Parts
- Electronic Parts
- Electrical Insulation
- Pressure Sensitive Tape
- Fiber Optics Cable
- Insulation Blankets
- Insulation Tubing
- Automotive Diaphragms Sensors and Manifolds
- Etching
General Information
| Item Name | Polyimide Film |
| Trade Name | Kapton® |
| Series | Kapton® HN-ROL |
General Features
| Type | General Purpose |
Performance Details
| Tensile Strength | 139 Mpa |
Physical Properties
| Elongation | 72 to 83% |
| Length | 1700 ft |
| Thickness | 1 mil |
| Width | 0.32 Inch |
| Density | 1.42 g/cc |