Von Roll/John C Dolph Dolphon® CC-1105-LV Polyester Resin
- MFR #Dolphon® CC-1105-LV
- EIS #PH21-Dolphon CC-1105-LV
$231.79 - $366.44
Refine your product below or compare all choices in the
Min QTY1QTY Increment1more infoPack--
Von Roll/John C Dolph Dolphon® CC-1105-LV Polyester Resin, 9.6 - 10.0 lb/gal At 77 °F (25 °C) Density, 3000 V/Mil Dielectric Strength, >200 °F Flash Point, 110 - 180 min At 212 °F Gel Time, 0.53 BTU/HR/ft²/Inch/°F Thermal Conductivity, 200 - 300 cps 10 rpm At 77 °F (25 °C) Viscosity. - CC-1105-LV is the single best selling electrical impregnation resin on the market. It is a versatile, cost-effective solventless polyester resin, offering excellent tank stability and superior performance characteristics.
Features
- High flash point (over 200 °F)
- Solventless
- Versatile - can be used in dip and bake, vacuum, VPI, rollthru and trickle applications
- Included in UL-approved systems up to 220 °C
- Exceptionally high bond strength
- Low VOC emissions
- Low viscosity-excellent penetration into windings
- Excellent tank stability
- Very low build - minimum clean-up and balancing
- Low odor
- Superior chemical resistance
- Excellent for vacuum processing because of low vapor pressure
- 1.5 x 10^14 Ohm at 500V surface resistivity
- 6.2 x 10^15 Ohm volume resistivity
- Flash Point: >200 °F
- Viscosity: 200 - 300 cps 10 rpm at 77 °F/25 °C
- Density: 9.6 - 10.0 lb/gal at 77 °F (25 °C)
- Thermal Conductivity: 0.53 BTU/HR/ft²/Inch/°F
- Gel Time: 110 - 180 min
- Viscosity: 200 - 300 cP
Applications
- Solenoids
- Transformers
- Rotors
- Armatures
- Inductors
- Form Wound Coils
- Ferro Resonant Transformers
- Stators
- Motors
- Chokes
- Brake Coils
- Hermetic Applications
General Information
| Item Name | Polyester Resin |
| Trade Name | Dolphon® |
| Series | Dolphon® CC-1105-LV |
Design & Construction
| Color | Clear/Amber |
Performance Details
| Gel Time | 110 min |
Technical Details
| Flash Point | 200 °F |
Chemical Properties
| Viscosity | 200 cP |
Electrical Properties
| Dielectric Strength | 3000 V/mil |
Documents
No Documents Found