Elantas PDG Pedigree® C 59 M Two-Component Hardener
MFR #:Pedigree® C 59 M
EIS #:PH21-Pedigree C 59 M
MFR #:Pedigree® C 59 M
EIS #:PH21-Pedigree C 59 M
Elantas PDG Pedigree® C 59 M Two-Component Hardener, Room Temperature Cure Type, 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water) Dielectric Strength, 171 °C (ASTM D93) Flash Point, 5 - 10 min At 25 °C/77 °F Gel Time, 77 Shore D At 25 °C/77 °F Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener Mixing Ratio, 0.998 (68 °F (20 °C)) Specific Gravity, 200 - 300 CP At 25 °C/77 °F Viscosity, 300 - 400 CP At 25 °C/77 °F Viscosity - Part-A, 40 - 70 CP At 25 °C/77 °F Viscosity - Part-B. - Pedigree® E 58 / C 59M is a two-component, fast curing, epoxy impregnating resin, moisture and chemical-resistant, low viscosity for good penetration.
$38.71
- $55.43
Select from the options below
Elantas PDG Pedigree® C 59 M Two-Component Hardener, Room Temperature Cure Type, 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water) Dielectric Strength, 171 °C (ASTM D93) Flash Point, 5 - 10 min At 25 °C/77 °F Gel Time, 77 Shore D At 25 °C/77 °F Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener Mixing Ratio, 0.998 (68 °F (20 °C)) Specific Gravity, 200 - 300 CP At 25 °C/77 °F Viscosity, 300 - 400 CP At 25 °C/77 °F Viscosity - Part-A, 40 - 70 CP At 25 °C/77 °F Viscosity - Part-B. - Pedigree® E 58 / C 59M is a two-component, fast curing, epoxy impregnating resin, moisture and chemical-resistant, low viscosity for good penetration.
Product Options
Showing 1 out of 1 options
 | Container Size: 8.26 lb | EIS Part #: PDGC59MG | $ / US pound |
- Attributes
- Features
- Applications
- Documents
Attributes
General Information
Item NameHardener
Trade NamePedigree®
SeriesPedigree® C 59 M
General Features
Net Weight8.2 - 8.4 lb/gal
Shelf Life12 Months
TypeTwo-Component
Design & Construction
Cure TypeRoom Temperature
FormLiquid
Performance Details
Gel Time5 min
Technical Details
Flash Point171 °C
Chemical Properties
Specific Gravity0.998
Viscosity200 cP
Viscosity - Part-A300 cP
Viscosity - Part-B40 cP
Mixing Ratio100 (Parts By Weight and Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener
Electrical Properties
Dielectric Strength1600 V/mil
Physical Properties
Hardness77 Shore D at 25 °C/77 °F
Features
- Rapid cure on room-temperature or preheated units with no oven bake
- High bond strength
- Meter-mix - trickle application method
- Twisted coil bond strength ASTM D4882 over MW 35: 97 pounds at 25 °C / 77 °F, 13 pounds at 150 °C / 302 °F
- 57 °C (DSC) glass transition temperature
- 99 ppm / °C (below Tg), 230 ppm / °C (above Tg) coefficient of thermal expansion
- 0.9% at ASTM D570 - 25 °C / 77 °F water absorption
- 4.3 x 10^13 ohm-cm at 25 °C / 77 °F, 3.3 x 10^11 ohm-cm at 100 °C / 212 °F volume resistivity
- 4.0 at 1 kHz - 25 °C / 77 °F, 6.6 at 1 kHz - 100 °C / 212 °F dielectric constant
- 0.02 at 1 kHz - 25 °C / 77 °F, 0.27 at 100 °C / 212 °F dissipation factor
- Secondary insulation
- Gel Time: 5 - 10 min
- Viscosity: 200 - 300 cP
- Viscosity - Part-A: 300 - 400 cP
- Viscosity - Part-B: 40 - 70 cP
Applications
- For Impregnation of Motor Armatures and Stators