Elantas PDG Pedigree® E58 Two-Component Epoxy Impregnating Resin
MFR #:Pedigree® E58
EIS #:PH21-Pedigree E58
MFR #:Pedigree® E58
EIS #:PH21-Pedigree E58
Elantas PDG Pedigree® E58 Two-Component Epoxy Impregnating Resin, Epoxy Base Type, Room Temperature Cure Type, 1.1582 g/cm3 (77 °F (25 °C)) Density, 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water) Dielectric Strength, 90 °C (ASTM D93) Resin, 171 °C (ASTM D93) Hardener Flash Point, 5 - 10 min At 25 °C/77 °F Gel Time, 77 Shore D At 25 °C/77 °F Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener Mixing Ratio, 300 - 400 CP At 25 °C/77 °F Viscosity, 300 - 400 CP At 25 °C/77 °F Viscosity - Part-A, 40 - 70 CP At 25 °C/77 °F Viscosity - Part-B. - Pedigree® E 58 / C 59M is a two-component, fast curing, epoxy impregnating resin, moisture and chemical-resistant, low viscosity for good penetration.
$35.74
- $48.57
Select from the options below
Elantas PDG Pedigree® E58 Two-Component Epoxy Impregnating Resin, Epoxy Base Type, Room Temperature Cure Type, 1.1582 g/cm3 (77 °F (25 °C)) Density, 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water) Dielectric Strength, 90 °C (ASTM D93) Resin, 171 °C (ASTM D93) Hardener Flash Point, 5 - 10 min At 25 °C/77 °F Gel Time, 77 Shore D At 25 °C/77 °F Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener Mixing Ratio, 300 - 400 CP At 25 °C/77 °F Viscosity, 300 - 400 CP At 25 °C/77 °F Viscosity - Part-A, 40 - 70 CP At 25 °C/77 °F Viscosity - Part-B. - Pedigree® E 58 / C 59M is a two-component, fast curing, epoxy impregnating resin, moisture and chemical-resistant, low viscosity for good penetration.
Product Options
Showing 2 out of 2 options
 | Container Size: 48 lb | EIS Part #: PDGE58PAIL | $ / US pound | |
| Container Size: 532 lb | EIS Part #: E58532LB | $ / US pound |
- Attributes
- Features
- Applications
- Documents
Attributes
General Information
Item NameEpoxy Impregnating Resin
Trade NamePedigree®
SeriesPedigree® E58
General Features
Shelf Life12 Months
TypeTwo-Component
Design & Construction
Base TypeEpoxy
Cure TypeRoom Temperature
FormLiquid
Performance Details
Gel Time5 min
Chemical Properties
Viscosity300 cP
Viscosity - Part-A300 cP
Viscosity - Part-B40 cP
Mixing Ratio100 (Parts By Weight and Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener
Electrical Properties
Dielectric Strength1600 V/mil
Physical Properties
Hardness77 Shore D at 25 °C/77 °F
Features
- Rapid cure on room-temperature or preheated units with no oven bake
- High bond strength
- Meter-mix - trickle application method
- Store below 25 °C / 77 °F in a dry controlled environment out of direct sunlight
- Twisted coil bond strength ASTM D4882 over MW 35: 97 pounds at 25 °C / 77 °F, 13 pounds at 150 °C / 302 °F
- 57 °C (DSC) glass transition temperature
- 99 ppm / °C (below Tg), 230 ppm / °C (above Tg) coefficient of thermal expansion
- 0.9% at ASTM D570 - 25 °C / 77 °F water absorption
- 4.3 x 10^13 ohm-cm at ASTM D257 - 25 °C / 77 °F, 3.3 x 10^11 ohm-cm at ASTM D257 - 100 °C / 212 °F volume resistivity
- 4.0 at 1 kHz - 25 °C / 77 °F, 6.6 at 1 kHz - 100 °C / 212 °F dielectric constant
- 0.02 at 1 kHz - 25 °C / 77 °F, 0.27 at 1 kHz - 100 °C / 212 °F dissipation factor
- Secondary insulation
- Dielectric Strength: 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water)
- Flash Point: 90 °C (ASTM D93) Resin, 171 °C (ASTM D93) Hardener
- Viscosity: 300 - 400 CP at 25 °C/77 °F
- Density: 1.1582 g/cm3 (77 °F (25 °C))
- Viscosity - Part-B: 40 - 70 CP at 25 °C/77 °F
- Gel Time: 5 - 10 min
- Viscosity: 300 - 400 cP
- Viscosity - Part-A: 300 - 400 cP
- Viscosity - Part-B: 40 - 70 cP
Applications
- Impregnation of Motor Armatures and Stators