Elantas PDG Sterling® E814 Single-Component Thermopoxy Impregnating Resin, 1.0724 g/cm3 (77 °F (25 °C)) Density, 4% At 25 °C/77 °F Elongation, >94 °C (ASTM D93) Flash Point, 12 - 16 hr At 100 °C/212 °F or 6 hr At 135 °C/275 °F Full Cure Time, 500 - 800 min At 100 °C/212 °F, 80 - 120 min At 125 °C/257 °F, 30 - 45 min At 150 °C/302 °F Gel Time, 72 Shore D - 25 °C/77 °F Hardness, 6800 psi Tensile Strength, 1000 - 1500 CP At 25 °C/77 °C Viscosity. - Sterling® E 814 is a single-component, heat cured, epoxy impregnating resin.
$47.19 / US pound
Min Qty:1
|Qty Increment:1
more info
more info
Elantas PDG Sterling® E814 Single-Component Thermopoxy Impregnating Resin, 1.0724 g/cm3 (77 °F (25 °C)) Density, 4% At 25 °C/77 °F Elongation, >94 °C (ASTM D93) Flash Point, 12 - 16 hr At 100 °C/212 °F or 6 hr At 135 °C/275 °F Full Cure Time, 500 - 800 min At 100 °C/212 °F, 80 - 120 min At 125 °C/257 °F, 30 - 45 min At 150 °C/302 °F Gel Time, 72 Shore D - 25 °C/77 °F Hardness, 6800 psi Tensile Strength, 1000 - 1500 CP At 25 °C/77 °C Viscosity. - Sterling® E 814 is a single-component, heat cured, epoxy impregnating resin.
- Attributes
- Features
- Applications
- Documents
Attributes
General Information
Item NameThermopoxy Impregnating Resin
Trade NameSterling®
SeriesSterling® E814
General Features
Net Weight8.9 lb/gal
Shelf Life3 Months
TypeSingle-Component
Design & Construction
FormLiquid
Performance Details
Tensile Strength6800 psi
Full Cure Time12 - 16 hr at 100 °C/212 °F or 6 hr at 135 °C/275 °F
Gel Time500 min
Technical Details
Flash Point94 °C
Chemical Properties
Viscosity1000 cP
Physical Properties
Container Size45 lb
Container TypePail
Elongation4% at 25 °C/77 °F
Hardness72 Shore D at 25 °C/77 °F
Features
- Low viscosity
- Capable of low temperature cure
- No catalyst required
- Dip-and-bake, vacuum-pressure impregnation, vacuum impregnation and potting application methods
- Store below 25 °C / 77 °F in a dry controlled environment out of direct sunlight
- 0.5% linear shrinkage
- 2.1% (168 hours @ 180 °C / 356 °F) weight loss
- 7.4 x 10^13 ohm-cm at ASTM D257 - 30 °C / 86 °F, 4.3 x 10^11 ohm-cm at ASTM D257 - 100 °C / 212 °F, 4.8 x 10^10 ohm-cm at ASTM D257 - 100 °C / 212 °F volume resistivity
- 3.1 at 60 Hz - 30 °C / 86 °F, 4.3 at 60 Hz - 100 °C / 212 °F, 4.3 at 60 Hz - 125 °C / 257 °F dielectric constant
- 0.002 at 60 Hz - 30 °C / 86 °F, 0.02 at 60 Hz - 100 °C / 212 °F, 0.15 at 60 Hz - 125 °C / 257 °F dissipation factor
- Secondary insulation
- Container Size: 45 lb/5 gal
- Flash Point: >94 °C (ASTM D93)
- Viscosity: 1000 - 1500 CP at 25 °C/77 °C
- Density: 1.0724 g/cm3 (77 °F (25 °C))
- Gel Time: 500 - 800 min
- Viscosity: 1000 - 1500 cP
Applications
- Impregnation of Transformers, Motor Windings and Form-Wound Coils, Especially High Voltage Coils Where Complete Penetration and Fill are Required, Excellent for Sand-Filled Potted Units