Elantas PDG Elan-Cast® C-110 Hardener, 2.5 lb/1 gal
MFR #:119385
EIS #:PDGC1103LB
MFR #:119385
EIS #:PDGC1103LB
Out of Stock
Min Qty:1
|Qty Increment:1
Elantas PDG Elan-Cast® C 110 Hardener, Room Temperature Cure Type, 0.9531 g/cm3 (77 °F (25 °C)) Density, 580 V/Mil (ASTM D149 - 50 Mil), 560 V/Mil (ASTM D149 - 50 Mil After 24 hr in Water) Dielectric Strength, 5% Elongation, >94 °C (ASTM D93) Flash Point, 16 hr At 60 °C/140 °F or 2 hr At 100 °C/212 °F Full Cure Time, 30 - 50 min At 25 °C/77 °F (200 ml) Gel Time, 85 Shore D Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 35 (Parts By Volume) Hardener Mixing Ratio, 5050 psi Tensile Strength, 0.4 W/mK Thermal Conductivity, 1500 - 2500 CP At 25 °C/77 °F Viscosity, 8500 - 13500 CP At 25 °C/77 °F Viscosity - Part-A, 200 - 300 CP At 25 °C/77 °F Viscosity - Part-B. - ELAN-Cast® E 297/C 110 epoxy is a two-component, room temperature curing, 100% solids resin system.
$63.58 / US pound
Min Qty:1
|Qty Increment:1
Elantas PDG Elan-Cast® C 110 Hardener, Room Temperature Cure Type, 0.9531 g/cm3 (77 °F (25 °C)) Density, 580 V/Mil (ASTM D149 - 50 Mil), 560 V/Mil (ASTM D149 - 50 Mil After 24 hr in Water) Dielectric Strength, 5% Elongation, >94 °C (ASTM D93) Flash Point, 16 hr At 60 °C/140 °F or 2 hr At 100 °C/212 °F Full Cure Time, 30 - 50 min At 25 °C/77 °F (200 ml) Gel Time, 85 Shore D Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 35 (Parts By Volume) Hardener Mixing Ratio, 5050 psi Tensile Strength, 0.4 W/mK Thermal Conductivity, 1500 - 2500 CP At 25 °C/77 °F Viscosity, 8500 - 13500 CP At 25 °C/77 °F Viscosity - Part-A, 200 - 300 CP At 25 °C/77 °F Viscosity - Part-B. - ELAN-Cast® E 297/C 110 epoxy is a two-component, room temperature curing, 100% solids resin system.
- Attributes
- Features
- Documents
Attributes
General Information
Item NameHardener
Trade NameElan-Cast®
SeriesElan-Cast® C-110
General Features
Net Weight7.8 - 8.1 lb/gal
Shelf Life12 Months
Design & Construction
Cure TypeRoom Temperature
FormLiquid
Performance Details
Tensile Strength5050 psi
Full Cure Time16 hr at 60 °C/140 °F or 2 hr at 100 °C/212 °F
Gel Time30 min
Thermal Conductivity0.4 W/mK
Technical Details
Flash Point94 °C
Chemical Properties
Viscosity1500 cP
Viscosity - Part-A8500 cP
Viscosity - Part-B200 cP
Mixing Ratio100 (Parts By Weight and Volume) Resin, 20 (Parts By Weight) 35 (Parts By Volume) Hardener
Electrical Properties
Dielectric Strength580 V/mil
Physical Properties
Container Size2.5 lb
Elongation5%
Hardness85 Shore D
Features
- Excellent electrical properties
- Mineral-filled for improved heat dissipation
- Low shrinkage
- Fast curing at room temperature
- Bench casting / potting, vacuum casting / potting application methods
- Tensile modulus: 93,000 PSI (ASTM D638)
- 57 °C (DSC) glass transition temperature
- 50 ppm / °C (below Tg), 155 ppm / °C (above Tg) coefficient of thermal expansion
- 3.5 at 1 kHz - 25 °C / 77 °F, 4.7 at 1 kHz - 100 °C / 212 °F, 6.8 at 1 kHz - 150 °C / 302 °F dielectric constant
- 0.01 at 1 kHz - 25 °C / 77 °F, 0.06 at 1 kHz - 100 °C / 212 °F, 0.21 at 1 kHz - 150 °C / 302 °F dissipation factor
- 4.2 x 10^15 Ohm-cm at 25 °C / 77 °F volume resistivity
- Gel Time: 15 - 25 min at 25 °C/77 °F (250 g)
- Container Size: 2.5 lb/1 gal
- Dielectric Strength: 580 V/Mil (ASTM D149 - 50 Mil), 560 V/Mil (ASTM D149 - 50 Mil After 24 hr in Water)
- Flash Point: >94 °C (ASTM D93)
- Viscosity: 1500 - 2500 CP at 25 °C/77 °F
- Density: 0.9531 g/cm3 (77 °F (25 °C))
- Viscosity - Part-B: 200 - 300 CP at 25 °C/77 °F
- Gel Time: 30 - 50 min
- Viscosity: 1500 - 2500 cP
- Viscosity - Part-A: 8500 - 13500 cP
- Viscosity - Part-B: 200 - 300 cP